Investigation of microstructure and mechanical properties of Cu/Ti-B-SiCP hybrid composites

ŞAP S., Turgut A., UZUN M.

CERAMICS INTERNATIONAL, cilt.47, sa.21, ss.29919-29929, 2021 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 47 Sayı: 21
  • Basım Tarihi: 2021
  • Doi Numarası: 10.1016/j.ceramint.2021.07.165
  • Dergi Adı: CERAMICS INTERNATIONAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, INSPEC, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.29919-29929
  • Anahtar Kelimeler: Composite materials, Copper, Powder metallurgy, Microstructure, Mechanical properties, METAL-MATRIX COMPOSITES, CARBON NANOTUBE, CU, TI, CARBIDE, EVOLUTION, GRAPHITE, BORON, SIZE
  • İnönü Üniversitesi Adresli: Evet

Özet

In this study, Cu/Ti-B-SiCp hybrid composite materials were produced by powder metallurgy method using three different sintering temperatures (950, 1000, 1050 degrees C). The optimum sintering temperature of Cu main matrix composites reinforced with Ti-B-SiCp reinforcement materials at 2-4-6-8 wt.% were determined and their microstructure and mechanical properties were investigated. As a result of microstructure studies, it was determined that reinforcement elements have a homogeneous interface in the main matrix. The hardness of the produced composites was determined by the Brinell hardness method. The highest hardness value (77.74 HB) was determined in the sample with 6 wt% reinforcement ratio. In the tensile and three point bending tests, maximum strength values (112.96 MPa, 37.76 MPa) were found in samples with a reinforcement ratio of 4 wt%. It was determined that increasing reinforcement ratios and sintering temperature made a positive contribution to the hybrid composite materials produced.