Enhancement of Magnetic and Transport Properties of Superconducting Fe1-xMnxSe0.5Te0.5 Single Crystals

Ozabaci M., Yakinci K., Yakinci M. E.

JOM, cilt.71, sa.9, ss.3285-3292, 2019 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 71 Sayı: 9
  • Basım Tarihi: 2019
  • Doi Numarası: 10.1007/s11837-019-03651-0
  • Dergi Adı: JOM
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.3285-3292
  • İnönü Üniversitesi Adresli: Evet

Özet

In this article, we provide the synthesis and characterization of manganese-substituted FeSe0.5Te0.5 single crystals in the nominal composition range of Fe1-xMnxSe0.5Te0.5 (x = 0.01, 0.05, 0.1) via the self-flux method. It is observed that Mn-substitution improved the bulk superconducting properties of FeSe0.5Te0.5 considerably by increasing the superconducting transition temperatures determined from both resistive and magnetic transitions. Our results reveal that x = 0.05 Mn-substituted sample yields the most appropriate superconducting performance, considering all the samples employed. The corresponding value is computed to be 4.7 x 10(4) A/cm(2) for x = 0.05 sample at 8 K under 0.2 kOe, and it decreases to the values 2.54 x 10(4) A/cm(2) and 1.34 x 10(4) A/cm(2) for the x = 0.01 and x = 0.1 samples, respectively.