Magnetic and Magnetocaloric Properties of (Gd1-xCex)Al-2 (x=0, 0.25, 0.5, 0.75) Compounds
JOURNAL OF MAGNETICS, vol.16, no.4, pp.337-341, 2011 (SCI-Expanded, Scopus)
- Publication Type: Article / Article
- Volume: 16 Issue: 4
- Publication Date: 2011
- Doi Number: 10.4283/jmag.2011.16.4.337
- Journal Name: JOURNAL OF MAGNETICS
- Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Page Numbers: pp.337-341
- Inonu University Affiliated: Yes
Abstract
The magnetic and magnetocaloric properties of Gd1-xCexAl2 (x = 0, 0.25, 0.5, 0.75) intermetallic compounds alloys have been investigated in detail for the first time. XRD patterns indicated that all the samples were crystallized in a single phase with MgCu2-type structure (Laves phase). Ce substitution for Gd increased the lattice parameters and decreased the Curie temperature from 163 K for x = 0 to 37 K for x = 0.75. A maximum entropy change of 3.82 J/kg K was observed when a 2 T magnetic field was applied to the x = 0 sample. This entropy change decreased with increasing Ce content to 2.04,J/kg K for the x = 0.75 sample.