CONSTRUCTION AND BUILDING MATERIALS, cilt.438, ss.1-17, 2024 (SCI-Expanded)
Over the last 20 years, the development of electrically conductive composites for removing snow and ice from transportation infrastructure has received exceptional traction. However, these composites need to exhibit stable electrical conductivity and high mechanical properties to be sustainable and cost-effective. Towards this goal, the article investigates the roles of ground granulated blast furnace slag (BFS) and copper slag (CS) content, in addition to hooked-end steel fiber length, on the electrical properties of eco-friendly ultra-high performance hybrid fiber-reinforced self-compacting concrete (HFR-SCC) for the first time in the literature. For this purpose, sixteen eco-friendly electrically conductive ultra-high-performance HFR-SCC were designed based on the variable parameters of four different BFS/total binder ratios (20, 40, 60, and 80 %), a CS/total fine aggregate ratio of 50 %, and two different hooked-end fiber lengths (30 and 60 mm), while all mixes used 1.75 % by volume fraction of steel fibers. After determining the workability properties (slump-flow and T500 values) of all mixes, compressive strength and electrical resistivity/conductivity tests of 90-day specimens were conducted. Additionally, environmental and economic evaluations of all mixes in terms of sustainability were performed in order to clarify the effects of the variable parameters. Taking into account the experimental results obtained, it was observed that all electrically conductive ultra-high performance HFR-SCC mixes demonstrated satisfactory workability properties, while the compressive strength values reached to impressive values of 127 MPa. The optimum BFS/total binder ratio was identified to be 40 % for higher compressive strength and conductivity of ultra-high performance HFR-SCC specimens. On the other hand, the addition of CS to the mixes resulted in an increase of almost 9 % in compressive strength compared to one without CS, while at the same time, a significant increase of approximately 363 % was observed in the electrical conductivity values of the specimens. As for the influence of different lengths of hooked steel fibers, the use of 30 mm length hooked-end steel fibers in HFR-SCC mixes performed better in terms of compressive strength, whereas 60 mm fibers performed better regarding electrical conductivity. In conclusion, this experimental work has evidenced that it is possible to develop an eco- friendly and sustainable electrically conductive ultra-high performance cementitious composite (the optimal mix compressive strength and electrical resistivity values were 127 MPa and 2242 Ω.cm, respectively) by using waste from different industries such as iron and copper. Thus, it will provide important insights for the design and application of future electrically conductive concretes, which can be an important alternative in efficient active deicing and snow-melting applications.