Giant magnetoimpedance effect in electroplated CoNiFe/Cu wires with varying Ni, Fe and Co content


Atalay F., KAYA H., ATALAY S.

JOURNAL OF ALLOYS AND COMPOUNDS, cilt.420, ss.9-14, 2006 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 420
  • Basım Tarihi: 2006
  • Doi Numarası: 10.1016/j.jallcom.2005.10.022
  • Dergi Adı: JOURNAL OF ALLOYS AND COMPOUNDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.9-14
  • Anahtar Kelimeler: magetoimpedance effect, electroplate, FECONI FERROMAGNETIC TUBES, MAGNETO-IMPEDANCE, AMORPHOUS WIRES, PLATED WIRE, DOMAIN-STRUCTURE, ANISOTROPY, FILMS, GMI
  • İnönü Üniversitesi Adresli: Evet

Özet

Giant magnetoimpedance (GMI) behaviour has been studied for wires consisting of an 8.82-13.75 mu m thick magnetic layer containing either Co20.77Ni61.74Fe17.49,Co18.21Ni41.20Fe40.59,Co18.97Ni49.60Fe31.43,Co46.01Ni39.87Fe14.12 or Co33.67Ni51.44Fe14.89. These magnetic layers were electroplated onto a 50 mu m diameter Cu non-magnetic wire. A large and sensitive GMI effect (about a 257% magnetoimpedance ratio) with nearly no hysteresis has been found in Co18.97Ni49.60Fe31.43 wire at a 90 kHz ac driving current. Scanning electron microscopy (SEM) images showed that samples have globular and crack-free deposits with a grain size that varies between 3.06 and 9.17 mu m. (c) 2005 Elsevier B.V All rights reserved.