SUPERCONDUCTOR SCIENCE & TECHNOLOGY, cilt.13, sa.7, ss.955-963, 2000 (SCI-Expanded)
We have melt quenched a series of Ga substituted Bi2-xGaxSr2Ca2Cu3O10+y samples with the compositions with x = 0.2, 0.4, 0.6, 0.8 and 1.0. Microstructure, thermal properties including crystallization activation energy, magnetic and superconducting properties were investigated. We have found that Ga3+ ions have a solid solubility limit in the BSCCO system and this limit was passed at x = 0.6. Below this limit HTc BSCCO n = 3 phase was obtained, but after the solid solubility limit samples yield multiphase superconducting properties. Extended heat treatment at 840 degrees C displayed no suppression of the solid solubility Limit. The crystallization kinetic studies were investigated using non-isothermal kinetic models of Kissinger and Augis-Bennet. Higher crystallization activation energies, E-a, were obtained compared to unsubstituted BSCCO materials, glassification improved and glass handling time increased. The substitution had a slight effect on J(c), the flux pinning in the material was improved and better J(c) values were obtained below the solid solubility limit.