Durability of Engineered Cementitious Composites Incorporating High-Volume Fly Ash and Limestone Powder


Turk K., Kina C., Nehdi M.

SUSTAINABILITY, cilt.14, sa.16, ss.1-16, 2022 (SCI-Expanded)

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 14 Sayı: 16
  • Basım Tarihi: 2022
  • Doi Numarası: 10.3390/su141610388
  • Dergi Adı: SUSTAINABILITY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Social Sciences Citation Index (SSCI), Scopus, Aerospace Database, CAB Abstracts, Communication Abstracts, Food Science & Technology Abstracts, Geobase, INSPEC, Metadex, Veterinary Science Database, Directory of Open Access Journals, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.1-16
  • İnönü Üniversitesi Adresli: Evet

Özet

This study investigates the effects of using limestone powder (LSP) and high-volume fly ash (FA) as partial replacement for silica sand (SS) and portland cement (PC), respectively, on the durability properties of sustainable engineered cementitious composites (ECC). The mixture design of ECC included FA/PC ratio of 1.2, 2.2 and 3.2, while LSP was used at 0%, 50% and 100% of SS by mass for each FA/PC ratio. Freeze-thaw and rapid chloride ions penetrability (RCPT) tests were performed to assess the durability properties of ECC, while the compressive and flexural strength tests were carried out to appraise the mechanical properties. Moreover, mercury intrusion porosimetry (MIP) tests were performed to characterize the pore structure of ECC and to associate porosity with the relative dynamic modulus of elasticity, RCPT and mechanical strengths. It was found that using FA/PC ratio of more than 1.2 worsened both the mechanical and durability properties of ECC. Replacement of LSP for SS enhanced both mechanical strengths and durability characteristics of ECC, owing to refined pore size distribution caused by the microfiller effect. It can be further inferred from MIP test results that the total porosity had a vital effect on the resistance to freezing–thawing cycles and chloride ions penetration in sustainable ECC.