The effects of Zn/Fe co-dopants on the structural, thermal, magnetic, and in vitro biocompatibility properties of calcium pyrophosphate ceramics

Kebiroglu H., Ates T., BULUT N., ERCAN İ., Ercan F., Acari I. K., ...Daha Fazla

PHYSICA B-CONDENSED MATTER, cilt.643, 2022 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 643
  • Basım Tarihi: 2022
  • Doi Numarası: 10.1016/j.physb.2022.414123
  • Dergi Adı: PHYSICA B-CONDENSED MATTER
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, PASCAL, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, INSPEC, Metadex, Civil Engineering Abstracts
  • Anahtar Kelimeler: Ceramics, Calcium pyrophosphate, X-ray diffraction (XRD), Cell viability, IONS
  • İnönü Üniversitesi Adresli: Evet

Özet

In the present work, calcium pyrophosphate (CPP) samples co-doped with Zn and Fe were prepared by using a wet chemical method, and their thermal, magnetic, structural, morphologic, and in vitro biocompatibility properties were investigated for the first time. X-ray diffraction (XRD) results showed that a continuous decreasing trend in two lattice parameters, unit cell volume, and average crystallite size was observed with the increasing Zn content. Zn content affected the magnetic and thermal behaviors, cell viability property of the CPP, as well as morphology. The sample containing 0.22 at.% Zn and 0.22 at.% Fe showed the best biocompatibility among all the samples, and the higher amount of Zn caused the lower cell viability. The bandgap of the CPP decreased with adding of Zn, while the linear absorption coefficient value increased.