Solid state synthesis and characterization of bulk beta-FeSe superconductors


Onar K., Yakinci M. E.

JOURNAL OF ALLOYS AND COMPOUNDS, cilt.620, ss.210-216, 2015 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 620
  • Basım Tarihi: 2015
  • Doi Numarası: 10.1016/j.jallcom.2014.09.045
  • Dergi Adı: JOURNAL OF ALLOYS AND COMPOUNDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.210-216
  • İnönü Üniversitesi Adresli: Evet

Özet

Polycrystalline FeSe0.88 was synthesized by solid-state reaction method in sealed quartz tube at different heat heating cycles. The identification and characterization of FeSe0.88 samples were determined by X-ray Diffraction (XRD), Scanning Electron Microscope (SEM) and Energy Dispersive X-ray Spectroscopy (EDX). The electrical transport, magnetic and thermal transport properties of the obtained samples were also investigated. The results showed that the sensitivity of resistivity and magnetic susceptibility depends on heating cycles while the structural formation of samples does not. The upper critical field H-c2(0) has been determined with the magnetic field parallel to the sample surface and yielding a maximum value of 23.2 T. At the zero field coherence length, xi, value was calculated to be 3.33 nm. Calculated mu H-0(c2)(0)/k(B)T(c) rate indicated comparably higher value (3.17 T/K) than the Pauli limit (1.84 T/K) and obtained results were suggested unconventional nature of superconductivity in our samples. (C) 2014 Elsevier B.V. All rights reserved.