We have produced the (BiPb)(2)V (x) Sr2Ca3Cu4-y Ti (y) O12+delta compounds for x=0.05 and y=0, 0.05, 0.10 and 0.20 by glass-ceramic method. The effects of vanadium adding and Ti doping on the structure have been investigated by electrical resistance, scanning electron micrographs (SEM), XRD patterns and magnetic hysteresis loop measurements. It has been found that the high-T (c) superconducting phase, (2223), is formed in the samples annealed at 845 degrees C for 185, with concentration x=y=0.05. However, with increasing Ti doping the (2223) phase transforms into the (2212) phase. We have observed no superconducting properties for x=0.05 and y=0.20 compound. It has completely transformed to semiconductor.