Effect of different heat treatments on magnetoelastic properties of Fe-based amorphous wire


Atalay S., Adiguzel H., Kamer O.

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, cilt.304, ss.495-498, 2001 (SCI İndekslerine Giren Dergi) identifier identifier

  • Cilt numarası: 304
  • Basım Tarihi: 2001
  • Doi Numarası: 10.1016/s0921-5093(00)01502-1
  • Dergi Adı: MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
  • Sayfa Sayıları: ss.495-498

Özet

The field dependence of Young's modulus of Fe77.5Si7.5B15 amorphous ferromagnetic wires were studied in as-quenched state and after furnace, current and pulse annealing. In as-quenched state, the change in Young's modulus as a function of field is small due to induced large anisotropy during the quenching process. Annealing for short times is sufficient to remove most of the quenched stresses resulting in magnetic softening and large change in Young's modulus. Further furnace or current annealing leads to surface crystallization which develops an easy axis in the circumferential direction, but such an easy axis was not observed in pulse annealed samples.