Magnetoimpedance Effect on Single NiFe Nanowire
JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, cilt.30, sa.7, ss.1795-1800, 2017 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 30 Sayı: 7
- Basım Tarihi: 2017
- Doi Numarası: 10.1007/s10948-017-3977-9
- Dergi Adı: JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.1795-1800
- İnönü Üniversitesi Adresli: Evet
Özet
In this study, Ni82Fe18 nanowires were deposited on Au-coated porous anodic alumina oxide (AAO) template by electrochemically. Scanning electron microscopy showed that wires have diameters of about 250-310 nm and length of 50-60 mu m. NiFe nanowire arrays embedded in AAO were mechanically polished until nanowires appeared. Later, electrical contacts were made to a single nanowire using a focused ion beam (FIB) system. Magnetoimpedance (MI) properties of single nanowire were investigated, and nearly 3.5 % MI was observed at 4 GHz driving current frequency.