Magnetoimpedance effect in electroplated NiFeRu/Cu wire

Atalay F., Kaya H., Atalay S.

JOURNAL OF PHYSICS D-APPLIED PHYSICS, cilt.39, sa.3, ss.431-436, 2006 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 39 Sayı: 3
  • Basım Tarihi: 2006
  • Doi Numarası: 10.1088/0022-3727/39/3/001
  • Dergi Adı: JOURNAL OF PHYSICS D-APPLIED PHYSICS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.431-436
  • İnönü Üniversitesi Adresli: Evet

Özet

Magnetoimpedance (MI) and hysteresis loops were studied in electroplated Ni-79.1 Fe-20.9/Cu, Ni75.64Fe24.26Ru0.10/Cu, Ni79.51Fe20.31Ru0.18/Cu and Ni75.99Fe23.66Ru0.34/Cu wires. Scanning electron micrographs showed that crack-free electroplated wires were obtained with a smooth surface. The average grain size varied between 3 and 10 mu m for all samples. It was found that circumferential anisotropy was induced in all samples during the electroplating process. The maximum MI response was 459 % at a frequency of 90 kHz, 361 % at 110 kHz, 157 % at 100 kHz and 114 % at 340 kHz for Ni79.1Fe20.9/Cu, Ni75.64Fe24.26Ru0.10/Cu, Ni79.51Fe20.31Ru0.18/Cu and Ni75.99Fe23.66Ru0.34/Cu wires, respectively.